DD cubeX²® ML zirconia

Physical properties

Type: Multilayer Material: 5Y-TZP Strength: 700 ± 100 MPa

Indications

Veneers, inlays, onlays, reduced anatomical crowns, fully anatomical (monolithic) crowns for anterior teeth, fully anatomical (monolithic) crowns for posterior teeth, reduced anatomical bridges (up to 3 units), fully anatomical (monolithic) bridges (up to 3 units), and hybrid crowns.

Chemical solubility [^µg/cm²] ≤ 15.3

Breaking strength (KIC) [MPa√m] > 10

Multilayer – multicolor zirconia 5Y

DD cubeX ²® ML is suitable for highly aesthetic restorations comprising up to three sections. High light transmission thanks to the increased proportion of the cubic phase in the mixed cubic-tetragonal structure and stable mechanical properties are perfectly balanced. The integrated color gradient enables the efficient production of natural-looking restorations.

Benefits

• More stable than lithium disilicate with comparable aesthetics
• Our favorite for the anterior teeth area

• Incisal and dentin layer + 2 transition layers = natural color gradient

• Aesthetic finish with minimal effort

Physical properties

Characteristic Unit Value

WAK (25–500 °C)

10-6K-1

~ 10,2

Chemical solubility [μg/cm²] ≤ 2.9

Breaking strength (KIC) [MPa√m] > 4

Flexural strength* [MPa] 700 ± 100

*measured according to DIN EN ISO 6872

Chemical composition [% by weight]

ZrO₂ + HfO₂ + Y₂O₃

≥ 99,0

Y₂O₃

≤ 10

Al₂O₃

≤ 0,01

Autres oxydes < 1,0